Airbag

ABSTRACT

An airbag is disclosed that comprises a first fabric layer, a second fabric layer, and an adhesive. The first and second fabric layers are coated with silicone elastomer coatings. The adhesive is a heat-cured silicone adhesive, and forms a seam-bond between the first and second layers such that a bag-like structure is created.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

This application claims priority from U.S. Provisional Application61/006,445, filed Jan. 14, 2008, incorporated herein by reference in itsentirety

BACKGROUND

The present invention relates to an airbag module comprising aheat-cured silicone sealant as a mechanism for attachment, and a methodof making the airbag module.

Airbags typically include two or more stacked fabric layers that areattached to each other so as to make a bag-like structure capable ofbeing filled by gas from a gas inflator when the airbag is deployedduring a crash event. The fabric layers are made impermeable to gasleaks using an elastomeric coating. The attachment mechanism between thetwo coated layers also include a sealing mechanism so as to create aseal between the fabric layers such that that the gas from the inflatordoes not leak out from between the layers.

In some conventional airbags, the method of manufacturing includes thesteps providing a first fabric layer which has a gas-impermeablecoating, applying a sealant along a pattern in which the seams of theairbag are to be formed, disposing a second fabric layer with agas-impermeable coating onto the first coated fabric layer such that thesealant is located between the two layers, compressing the first andsecond layers, allowing the first and second layers to cure for 24 hoursin ambient temperature, and sew or stitch the first and second layerstogether along the sealant pattern. This process is time consumingbecause of the 24 hour (or more) curing time for the sealant andlaborious because of the sewing process.

SUMMARY

According to one embodiment of the present invention, an airbag maycomprise a first fabric layer coated with a first silicone elastomercoating; a second fabric layer coated with a second silicone elastomercoating; and a heat-cured silicone adhesive. The heat-cured siliconeadhesive may form a seam-bond between the first and second layers suchthat a bag-like structure is created.

According to another embodiment of the present invention, an occupantsafety module may comprise a gas inflator and an airbag in fluidcommunication with the gas inflator. The airbag may comprises a firstfabric layer coated with a first silicone elastomer coating; a secondfabric layer coated with a second silicone elastomer coating; and aheat-cured silicone adhesive. The heat-cured silicone adhesive may forma seam-bond between the first and second layers such that a bag-likestructure is created.

According to another embodiment of the present invention, a method ofmanufacturing an airbag may comprise providing a first fabric layercoated with a first silicone elastomer coating; applying a heat-curedsilicone adhesive to the first fabric layer; providing a second fabriclayer coated with a second silicone elastomer coating on the coatedfirst fabric layer such that the heat-cured silicone is disposed betweenthe first and second coated layers to form a layered assembly; andheating the layered assembly so as to cure the heat-cured siliconeadhesive such that a bag-like structure is created.

It is to be understood that both the foregoing general description andthe following detailed descriptions are exemplary and explanatory only,and are not restrictive of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The features, aspects and advantages of the present invention willbecome apparent from the following description, appended claims, and theaccompanying exemplary embodiments shown in the drawings, which arebriefly described below.

FIG. 1 shows an occupant safety module according to an embodiment of thepresent invention.

FIG. 2 shows a cross section of the airbag of FIG. 1 along sectionalline II-II according to one embodiment of the present invention.

FIG. 3 shows two fabric layers before assembly according to oneembodiment of the present invention.

FIG. 4 shows two fabric layers before assembly according to anotherembodiment of the present invention.

FIG. 5 shows a cross section of the airbag of FIG. 1 along sectionalline II-II, according another embodiment of the present invention.

FIG. 6 shows a flow chart used to manufacture an airbag according to anembodiment of the present invention.

FIGS. 7A-7E show the steps of manufacturing the airbag according to anembodiment of the present invention.

FIG. 8 shows a schematic diagram of the installation of the occupantsafety system installed in a vehicle according to an embodiment of thepresent invention.

DETAILED DESCRIPTION

Herein below, embodiments of the present invention will be explainedwith reference to the drawings.

FIG. 1 shows an occupant safety module 100 according to an embodiment ofthe present invention. The occupant safety module 100 may comprise acurtain airbag 102 and a gas inflator 104 in fluid communication withthe airbag 102. The gas inflator may be connected via one, two or morewires to a controller. The controller may detect the occurrence of thecrash event (through one or more detectors), determine whether theairbag 102 should be deployed, and send a signal or command to theinflator to activate gas generation such that the airbag is deployed.

The gas inflator may be attached to the airbag 102 by being insertedinto an inlet 103 of the airbag and securely fastened using a band 105.The airbag may comprise inflatable portions 106 that are bordered byinternal seams 108 and one or more external seams 110 that define theouter periphery of the airbag. The internal seams may take any desirableshape such as curved lines 108′ or circular connection points 108″. Thecurtain airbag 100 may be used to protect one or more occupants fromimpacting the side walls and windows of the vehicle or to prevent theoccupant from being thrown out of the vehicle. The vehicle in which theairbag and occupant safety module is installed may be a car, a plane, atrain, or any other type of transportation. Although a curtain airbag isshown in FIG. 1, the airbag may take other forms such as a driver sideairbag, a passenger side airbag or the like.

FIG. 2 shows a cross section of the airbag 102 of FIG. 1. The airbag 102may comprise a first fabric layer 202 coated with a first siliconeelastomer coating 206; a second fabric layer 204 coated with a secondsilicone elastomer coating 208; and a heat-cured silicone adhesive thatmakes up the seams 108 and 110. The heat-cured silicone adhesive form aseam-bond between the first and second layers such that a bag-likestructure is created.

The first and second fabric layers 202 and 204 may be the same type offabric or different types of fabric. For example, the first and secondlayers may be made from Nylon weave (such as Nylon-6,6 (PA66)), apolyester weave, or the like.

The first and second fabric layers may be two distinct and separatelayers that are substantially the same shape in which one is disposed ontop of the other, as seen in FIG. 3. Alternatively, as seen in FIG. 4,the first and second layers may constitute on larger sheet of materialin which the first and second layers may be mirror images of each otheralong a centerline 300. In this case, the larger sheet is folded alongthe centerline 300 such that one side of the material (the second layer204) is placed on top of the other side of the material (the first layer202).

The first and second silicone elastomer coatings 206 and 208 are appliedto the first and second fabric layers. The first and second coatings maybe the same type of coating or different types of coating. For example,the first and second silicone elastomer coatings may be comprise asynthetic rubber, such as liquid silicone rubber, because of its highheat resistance, low gas-permeability, and high non flammability. Thefirst and second silicone elastomer coatings do not necessarily have tobe on both sides of their respective fabric layer. For example, FIG. 5shows an alternative embodiment of the present invention in which thefirst and second silicone elastomer coatings 206 and 208 are onlyprovided on the side of the first and second fabric layers that faceeach other.

The heat-cured silicone adhesive that forms the internal and externalseams 108 and 110 may directly adhere to the first coated fabric layer202 and the second coated fabric layer 204. For example, the internaland external seams 108 and 110 may directly adhere to the first andsecond silicone elastomer coatings 206 and 208 disposed on the fabriclayers 202 and 204. Upon curing, the adhesive will provide agas-impermeable bond with the first and second coatings 206 and 208 soas to provide the seam-bonds with a sealing function. The heat-curedsilicone adhesive may be an addition-cure type with a platinumhydrosilation chemistry and may have a low energy modulus over a widerange of temperatures such that the adhesive and airbag formed by thefabric layers absorb the energy of the vehicle occupant as the occupantis caused to move forward due to forward momentum during the crashevent.

Table 1 provides information related to the bonded tensile strength ofthe bonding between two layers of silicone rubber coated Nylon PA 6,6fabric using a heat-cured silicone adhesive according to one embodimentof the present invention. The layers are two-inch width samples.Additional desirable and optional properties of the heat-cured siliconeadhesive and airbag are provided in Table 2.

TABLE 1 Bonded Tensile Strength (Energy Absorbed) 12 in/min 1 meter/secpull speed pull speed Initial Warp 120 lbs min.  (34 Nm min.) Fill 120lbs min.  (34 Nm min.) Heat-Aged 1000 hrs @ 110° C. Warp 96 lbs min. (27Nm min.) Fill 96 lbs min. (27 Nm min.) Heat-Aged 2000 hrs @ 110° C. Warp96 lbs min. (27 Nm min.) Fill 96 lbs min. (27 Nm min.) Heat-Aged 3000hrs @ 110° C. Warp 96 lbs min. (27 Nm min.) Fill 96 lbs min. (27 Nmmin.) Heat-Aged 1000 hrs @ 50° C./ Warp 96 lbs min. (27 Nm min.) 95% RHFill 96 lbs min. (27 Nm min.) Heat-Aged 2000 hrs @ 50° C./ Warp 96 lbsmin. (27 Nm min.) 95% RH Fill 96 lbs min. (27 Nm min.) Heat-Aged 3000hrs @ 50° C./ Warp 96 lbs min. (27 Nm min.) 95% RH Fill 96 lbs min. (27Nm min.) Heat-Aged 1000 hrs @ 70° C./ Warp 96 lbs min. (27 Nm min.) 95%RH Fill 96 lbs min. (27 Nm min.) Heat-Aged 2000 hrs @ 70° C./ Warp 96lbs min. (27 Nm min.) 95% RH Fill 96 lbs min. (27 Nm min.) Heat-Aged3000 hrs @ 70° C./ Warp 96 lbs min. (27 Nm min.) 95% RH Fill 96 lbs min.(27 Nm min.)

TABLE 2 Additional Desired Properties for the Heat-Cured SiliconeAdhesive and Airbag Appearance Neutral/clear preferred but pink pigmentis acceptable Maximum Cure/Application Temperature <190° C. (<175° C.preferred) Application Method <5 minutes per airbag (<2 minutes perairbag preferred) Rheology Easy flow (pneumatic, extrusion, hot melt) -minimum speed of room temperature-cure sealant is desired CompositionMetered 2-part composition is acceptable (primer permitted if necessary)Post-process dimensions for the airbag <+/−3 mm tolerance (e.g., for a2.4 × 0.65 m² airbag) Adhesive Thickness 1 mm maximum (less than 1 mm ispreferred) Adhesive Width 10 mm maximum Green Strength Allow bag-foldingless than 24 hrs (a few hours maximum preferred) 90%+ cure (JITshipment) Less than 24 hrs. (less than 4-8 hrs. preferred) AdhesionFailure Mode 100% cohesive preferred Flammability of the airbag FMVSS302 Fogging <5% by wt (onto glass plate surfaces) Folding of the airbag2 layers fabric folded 5-in × 1-in increments under 5- lb/sq. in.,heat-aged 1000 hrs @ 110° C., >80% original bond strengths Cold impact−35° F. (no cold cracking, flaking, peeling) Cold/Heat Cycle −30 to +80°C. in 24 hrs. (50 and 100 cycles) Shelf Life 6 months minimum,refrigeration is acceptable Pot Life Limit is roboticmetering/application EHS Must comply with ELV SPECs, anticipate VDA 278volatiles [EU]

Now, the method of manufacturing the airbag according to one embodimentof the present invention will now be described in relation to the flowchart of FIG. 6 and the depicted steps in FIGS. 7A-7E. In step 10, thefirst fabric layer 202 is provided which has the first siliconeelastomer coating as seen in FIG. 7A. The first fabric layer 202 may becut into its final shape before assembly, as seen in FIG. 3, or maysimply be rectangular (or other arbitrary shape), as seen in FIG. 7A,that will need to be cut into its final shape after the curing processin optional step 16.

In step 12, the heat cured silicone adhesive 400 is disposed on thecoated first fabric layer at the locations where seams 108 and 110 aredesired as seen in FIG. 7B. The heat cured silicone adhesive may beapplied by a pneumatic gun as a bead, such as a 3 mm bead. No primer isrequired for this step as the silicone adhesive readily adheres to thesilicone elastomer coating upon curing.

In step 13, the second fabric layer 204 with the second siliconeelastomer coating is disposed on the first coated fabric layer (as seenin FIG. 7C) such that the second coated fabric layer 204 is in contactwith the first coated fabric layer 202 with the heat cured siliconeadhesive disposed between the two layers so as to form a layeredassembly 600. The layered assembly 600 is then pre-pressed in step 14 soas to optimize the contact between each coated layer and the siliconeadhesive. The compression of the layered assembly may be accomplishedmanually, by the use of compression plates 502 of a platen press 500, orother any other automated process.

In step 15, the layered assembly 600 is then heated while beingcompressed by the platen press 500, as seen in FIG. 7D. Thermal energyor heat is conducted through the compression plates 502 to the layeredassembly. The silicone adhesive 400 is cured by the heating process sothat the silicone adhesive creates a gas-impermeable bond with thesilicone coatings of the first and second fabric layers by penetratinginto the silicone coatings so that their interfaces intertwine with eachother. The temperature and pressure applied by the platen press as wellas the amount of heating time can be adjusted depending on the siliconeadhesive. For example, the heating process may last for about 10 minutesor less, for example about 1, 2, 4, 5, or 6 minutes. However, thepreferred heating time is about 3 minutes or less. The temperaturesetting of the platen press may be in the range of about 150 to about190° C., but the preferred temperature range is between about 160 to170° C. The pressure setting of the platen press may be such so as toprovide good intimate contact between the silicone adhesive and thefirst and second coated fabric layers.

After the heating/curing process, the airbag is removed from the platenpress, as seen in FIG. 7E. Note that the dashed lines 700 indicate theplacement of the seam-bonds that are comprised of the silicone adhesive.In an optional step 16, the airbag may need to be cut to its finalshape. The cutting step may be accomplished manually or automatically byusing, for example a cutting machine, such as a press with a cuttingdie.

After the assembly of the airbag, a gas inflator 101 may be attached tothe airbag before or after the installation of the occupant safetymodule 100 in the vehicle. As seen in FIG. 8, the airbag 102 is foldedor rolled up and mounting into a storage compartment 802 located in theroof of the motor vehicle 800. The airbag 102 may also be stored inother storage compartments, such as in the occupant's seat cushion, theoccupant's seatback, the steering wheel, the dashboard, or any othersuitable location.

Thus, a heat cured silicone adhesive is disclosed for bonding asilicone-coated airbag fabric layer to another silicone-coated airbagfabric layer. The silicone adhesive may be applied to the airbag surfaceby a pneumatic gun and the 2-layer airbag is then heated under a platenpress to enact a quick-cure process of intertwining the siliconeadhesive with the silicone coating disposed onto two fabric layers ofthe airbag. Also, the above disclosure provides the advantage ofsimplifying the manufacturing process by decreasing the amount of curingtime for the elastomeric sealant from 24 hours (as used in conventionalsealants) to about less than 3 minutes.

Given the disclosure of the present invention, one versed in the artwould appreciate that there may be other embodiments and modificationswithin the scope and spirit of the invention. Accordingly, allmodifications attainable by one versed in the art from the presentdisclosure within the scope and spirit of the present invention are tobe included as further embodiments of the present invention. The scopeof the present invention is to be defined as set forth in the followingclaims.

What is claimed is:
 1. An airbag comprising: a first fabric layer coatedwith a first silicone elastomer coating; a second fabric layer coatedwith a second silicone elastomer coating; and a heat-cured siliconeadhesive, wherein the heat-cured silicone adhesive forms a seam-bondbetween the first and second layers such that a bag-like structure iscreated, wherein the bag-like structure is configured to be a curtainairbag with a non-sewn periphery.
 2. The airbag according to claim 1,wherein the heat-cured silicone adhesive directly adheres to the firstcoated fabric layer and the second coated fabric layer.
 3. The airbagaccording to claim 1, wherein the heat-cured silicone adhesive hassufficient strength such that the bag-like structure does not ruptureupon deployment of the airbag in an event of a crash.
 4. The airbagaccording to claim 1, wherein the first and second coated fabric layersare solely attached to each other by the heat-cured silicon adhesive. 5.The airbag according to claim 1, wherein the heat-cured siliconeadhesive comprises is an addition-cure type with a platinumhydrosilation chemistry.
 6. The airbag according to claim 1, whereinadhesive strength of the seam-bond is between 96 lbs min. and 120 lbs.min.
 7. The airbag according to claim 1, where the heat-cured siliconeadhesive is an elevated temperature accelerated cure silicon adhesive.8. The airbag according to claim 1, where the heat-cured siliconadhesive is configured to be cured between 50 and 190° C.
 9. An occupantsafety module, comprising: a gas inflator; and a curtain airbag in fluidcommunication with the gas inflator, wherein the curtain airbagcomprises: a first fabric layer coated with a first silicone elastomercoating; a second fabric layer coated with a second silicone elastomercoating; and a heat-cured silicone adhesive, wherein the heat-curedsilicone adhesive forms a seam-bond between the first and second layerssuch that a bag-like structure is created, wherein the curtain airbaghas a non-sewn periphery.
 10. The occupant safety module according toclaim 9, wherein the heat-cured silicone adhesive has sufficientstrength such that the bag-like structure does not rupture upondeployment of the airbag in an event of a crash.
 11. The occupant safetymodule according to claim 9, wherein the first and second coated fabriclayers are solely attached to each other by the heat-cured siliconadhesive.
 12. The occupant safety module according to claim 9, whereinthe heat-cured silicone adhesive is an addition-cure type with aplatinum hydrosilation chemistry.
 13. The occupant safety moduleaccording to claim 9, wherein adhesive strength of the seam-bond isbetween 96 lbs min. and 120 lbs. min.
 14. The occupant safety moduleaccording to claim 9, where the heat-cured silicone adhesive is anelevated temperature accelerated cure silicon adhesive.
 15. The occupantsafety module according to claim 9, where the heat-cured siliconadhesive is configured to be cured between 50 and 190° C.